- Bolts[10]
- Metallurgy Machinery Parts[10]
- Nickel[10]
- Other Steel Products[10]
- Stainless Steel Wire[10]
- Flat Steel[10]
- Steel Round Bars[10]
- Steel Sheets[7]
- Steel Wire[10]
- Contact Person : Ms. Chen Grace
- Company Name : HY (Shanghai) Industry Co., Ltd.
- Tel : 0086-021-52286112
- Fax : 0086-021-52286112-802 Address: Room 202, No.34, 155 Nong South Lian hua Rd, Minhang District, Shanghai, China Zip: 200237 Country/Region: China (Mainland) Province/State: Shanghai
- Address : Shanghai,ShangHai,Room 202, No.34, 155 Nong South Lian hua Rd, Minhang District, Shanghai, China
- Country/Region : China
- Zip : 200237
Related Product Searches:Incoloy 901 bar,High Quality,incoloy 901 solution bright bar, round bar,Bar
Incoloy 901 Chemical composition:
Alloy | % | Ni | Cu | Al | Fe | Ti | Co | Mn | S | C | Si | P | Cr | Mo | B |
Incoloy 901 | Min. | 40.0 |
|
|
| 2.35 |
|
|
|
|
|
| 11.0 | 5.0 | 0.01 |
Max. | 45.0 | 0.50 | 0.35 | Balance | 3.10 | 1.0 | 1.0 | 0.03 | 0.10 | 0.60 | 0.03 | 14.0 | 7.0 | 0.02 |
Incoloy 901 Physical properties:
Density | 8.14 g/cm3 |
Melting point | 1280-1345°C |
Incoloy 901 minimum mechanical properties in the room temperature:
Status | Tensile strengthRm N/mm2 | Yield strengthRP0.2N/mm2 | ElongationA5 % |
Incoloy 901 | 1034 | 689 | 12 |
DescriptionA nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.Corrosion ResistanceAlloy 901 has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.Workability Hot WorkingAlloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range. WeldabilityAlloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.
Incoloy 901 bar